FR-4010(Aluminum diethyl phosphinate) |
|
Specifications |
ppearance |
Off white powder |
P(%) |
16 min |
Bulk density(g/㎤) |
0.65 |
Volatile(%) |
0.5 max |
Assay(%) |
99 min |
D50(㎛) |
3.5 max |
Decomposition temp(TGA) |
260°C(1% lost) |
|
|
Dosage |
Polymer |
Dosage(wt%)GFR-KS01
|
Grade |
1/16(TPE mixed) |
30 |
UL94-V0 |
1/16(TPU ester) |
15~20 |
UL94-V0 |
1/16(TPU ether) |
20~25 |
UL94-V0 |
|
|
成分Components |
|
(Modified Melamine Polyphosphate) CAS:218768-84-4
(Modified Melamine Pyrophosphate) CAS:15541-60-3
(Modified Aluminium tripolyphosphate)CAS:29196-72-3
(Silica dioxide) CAS:7631-86-9
|
|
|
Characteristics |
|
Preservation of initial surface conditions and keep good basic physical properties of the plastic materials.
High thermal stability for processing workability.
Its most important characteristics is forming very strong double layers coke shell.
No surface slippery feeling risk in the hot water test.
FR-4010 is Different from traditional phosphorus-nitrogen based flame retardants with good electric properties.
|
|
|
Suggestion |
|
The dosage is depended on wire & cable materials about 15wt% to 35wt% could achieve VW-1 grade.
No separate out, migration, blooming, and good water resistance.
Anti-dropping without adding any halogen agent.
FR-4010 performs extremely homogeneous mixbility in thermoplastic olefins.
Because many processing assistants may influence fire-proof performance of the plastic material, the amount of flame retardant added should be appropriately adjusted according to the actual situations.
|
|
|
Store |
|
Store in a dry & cool place, sealed.
|
|
|
Pack |
|
15 Kg in a PE-reinforced paper bag.
|
|
|
TPE Physical properties test |
Major physical properties |
Methods |
Units |
XX-2200 |
FR-4010 |
測試項目 |
Standars-ASTM |
Unit |
30wt% |
30wt% |
Polymer |
PP-SEBS |
- |
70wt% |
70wt% |
Form/Color |
目視 |
- |
黑色 |
黑色 |
Surface Hardness |
D2240 |
Shore-A |
86 |
87 |
Specific Gravity |
D792 |
g/㎤ |
1.19 |
1.17 |
MI (5kg,190℃) |
D1238 |
g/10min |
0.18 |
1.45 |
Tensile strength |
D412 |
kg/㎠ |
76 |
85 |
Tear strength |
D624 |
kg/cm |
35 |
39 |
Elongation at break |
D412 |
% |
987.2 |
763 |
UL94-V0(1.6") |
- |
- |
OK |
OK |
|
|
TPU Physical properties test |
Major physical properties |
Methods |
Units |
XX-2200 |
FR-4010 |
測試項目 |
Standars-ASTM |
Unit |
18wt% |
18wt% |
Polymer |
TPU |
- |
82wt% |
82wt% |
Form/Color |
目視 |
- |
黑色 |
黑色 |
Surface Hardness |
D2240 |
Shore-A |
86 |
86 |
Specific Gravity |
D792 |
g/㎤ |
1.34 |
1.33 |
MI (5kg,190℃) |
D1238 |
g/10min |
5.5 |
1.6 |
Tensile strength |
D412 |
kg/㎠ |
36 |
194 |
Tear strength |
D624 |
kg/cm |
22 |
63.9 |
Elongation at break |
D412 |
% |
187.2 |
530 |
UL94-V0(1.6") |
- |
- |
OK |
OK |
|
|